pH-Responsive Nanogels Generated by Polymerization-Induced Self-Assembly of a Succinate-Functional Monomer.

Colloidal nanogels formed from a pH-responsive poly(succinate)-functional core and a poly(sulfonate)-functional corona were prepared via a previously unreported reversible addition-fragmentation chain-transfer (RAFT)-mediated aqueous emulsion polymerization-induced self-assembly (PISA) route. Specifically, a poly(potassium 3-sulfopropyl methacrylate) (PKSPMA50) macromolecular chain-transfer agent (macro-CTA) was synthesized via RAFT solution polymerization followed by chain-extension with a hydrophobic, carboxylic acid-functional, 2-(methacryloyloxy) ethyl succinate (MES) monomer at pH 2. Colloidal nanoparticles with tunable diameters between 66 to 150 nm, depending on the core composition, and narrow particle size distributions were obtained at 20% w/w solids. Well-defined pH-responsive nanogels that swell on increasing the pH could be prepared even without the addition of a cross-linking comonomer, and introducing an additional cross-linker to the core led to smaller nanogels with lower swelling ratios. These nanogels could reversibly change in size on cycling the pH between acidic and basic conditions and remain colloidally stable over a wide pH range and at 70 °C.

Bridging Flocculation of a Sterically Stabilized Cationic Latex as a Biosensor for the Detection of Microbial DNA after Amplification via PCR.

There is a high demand for rapid, sensitive, and accurate detection methods for pathogens. This paper demonstrates a method of detecting the presence of amplified DNA from a range of pathogens associated with serious infections including Gram-negative bacteria, Gram-positive bacteria, and viruses. DNA is amplified using a polymerase chain reaction (PCR) and consequently detected using a sterically stabilized, cationic polymer latex. The DNA induces flocculation of this cationic latex, which consequently leads to rapid sedimentation and a visible change from a milky-white dispersion to one with a transparent supernatant, presenting a clear visible change, indicating the presence of amplified DNA. Specifically, a number of different pathogens were amplified using conventional or qPCR, including Staphylococcus aureus, Escherichia coli, and Herpes Simplex Virus (HSV-2). This method was demonstrated to detect the presence of bacteria in suspension concentrations greater than 380 CFU mL-1 and diagnose the presence of specific genomes through primer selection, as exemplified using methicillin resistant and methicillin susceptible Staphylococcus aureus. The versatility of this methodology was further demonstrated by showing that false positive results do not occur when a PCR of fungal DNA from C. albicans is conducted using bacterial universal primers.

Preparation of polymer nanoparticle-based complex coacervate hydrogels using polymerisation-induced self-assembly derived nanogels.

This paper reports a generic method to prepare polymer nanoparticle-based complex coacervate (PNCC) hydrogels by employing rationally designed nanogels synthesised by reversible addition-fragmentation chain-transfer (RAFT)-mediated polymerisation-induced self-assembly (PISA). Specifically, a poly(potassium 3-sulfopropyl methacrylate) (PKSPMA) macromolecular chain-transfer agent (macro-CTA) was synthesised via RAFT solution polymerisation followed by chain-extension with a statistical copolymer of benzyl methacrylate (BzMA) and methacrylic acid (MAA) at pH 2. Thus, pH-responsive nanoparticles (NPs) comprising a hydrophobic polyacid core-forming block and a sulfonate-functional stabiliser block were formed. With the introduction of methacrylic acid into the core of the NPs, they become swollen with increasing pH, as judged by dynamic light scattering (DLS), indicating nanogel-type behaviour. PNCC hydrogels were prepared by simply mixing the PISA-derived nanogels and cationic branched polyethyleneimine (bPEI) at 20% w/w. In the absence of MAA in the core of the NPs, gel formation was not observed. The mass ratio between the nanogels and bPEI affected resulting hydrogel strength and a mixture of bPEI and PKSPMA68-P(BzMA0.6-stat-MAA0.4)300 NPs with a mass ratio of 0.14 at pH ∼7 resulted in a hydrogel with a storage modulus of approximately 2000 Pa, as determined by oscillatory rheology. This PNCC hydrogel was shear-thinning and injectable, with recovery of gel strength occurring rapidly after the removal of shear.